Investigation of Inhibition Effect of Acrylic acid on C-Steel Corrosion in Sulfuric Acid Solutions

Authors

  • S. Abd El Wanees Chemistry Department, Faculty of Science, Tabuk University, Tabuk, Kingdom of Saudi Arabia Chemistry Department, Faculty of Science, Zagazig University, Zagazig 44519, Egypt
  • Salah Salem Tabuk University, Tabuk, Kingdom of Saudi Arabia
  • A.M.A A Shehata Faculty of Education45111, Suez Canal University, Al-Arish
  • M. Abd El Azim Menoufia University, Menoufia

DOI:

https://doi.org/10.24297/jac.v6i3.2643

Keywords:

Acrylic acid, Polymeric film, Corrosion inhibitor, Gasometry, Weight loss, Galvanostatic polarization and potentiodynamic

Abstract

Acrylic acid was tested as a corrosion inhibitor for C-steel in 0.5 M H2SO4 using gasometry, weight loss, and galvanostatic polarization techniques. Polymeric film is built up by cyclic voltammetry technique. The potentiodynamic polarization is used to examine the inhibition effect with the coated polymeric film. The data obtained from the different techniques coincide in that acrylic acid is a good mixed-type inhibitor. The inhibition process is based on the adsorption of acrylic acid on the surface of C-steel according to Temkin’s adsorption isotherm. The inhibition efficiency increases with inhibitor concentration and decreases with temperature. The thermodynamic parameters ΔE, ΔH*, ΔS*, and ΔG*ads were calculated to elaborate the mechanism of corrosion inhibition.

Downloads

Download data is not yet available.

Author Biographies

Salah Salem, Tabuk University, Tabuk, Kingdom of Saudi Arabia

Chemistry Department, Faculty of Science

A.M.A A Shehata, Faculty of Education45111, Suez Canal University, Al-Arish

Chemistry Department

M. Abd El Azim, Menoufia University, Menoufia

Department of Chemistry, Faculty of Science

Downloads

Published

2010-12-07

How to Cite

Wanees, S. A. E., Salem, S., A Shehata, A., & Azim, M. A. E. (2010). Investigation of Inhibition Effect of Acrylic acid on C-Steel Corrosion in Sulfuric Acid Solutions. JOURNAL OF ADVANCES IN CHEMISTRY, 6(3), 1059–1071. https://doi.org/10.24297/jac.v6i3.2643

Issue

Section

Articles