The Effect of Sodium Hydroxide Solutions with Different Ph on the Corrosion Of Iron Alloy (C1010) In Industrial Water

Authors

  • Mouayed yousif kadhum Department of Chemistry , College of Education for Pure Science , University of Basrah , Basrah , Iraq
  • Chasib Khaiber Bkhakh Industrial Water Section , Iraqi Drilling Company ,Northern Rumaila , Basrah , Iraq
  • Muayad Hasan Albehadili Department of Applied Marine Science, College of Marine Science , University of Basrah , Basrah , Iraq

DOI:

https://doi.org/10.24297/jac.v15i1.7134

Keywords:

Industrial water, pH, Tafel plot, Rate of corrosion, Drilling operation

Abstract

 The effect of increasing pH value in the corrosion of iron alloy type (C1010) was studied in the presence of different pH solutions of sodium hydroxide dissolved in industrial water at 35ËšC  and it was found that the corrosion rate of iron alloy was less at pH of 9.5 . This result was proved by measuring some thermodynamic parameters such as corrosion current and covered surface area that pertain to corrosion using weight loss electrical (Tafel plot ) methods . Also the effect of temperature on the rate of corrosion at ( 25ËšC , 35ËšC and 45ËšC ) at different pH was studied and it was found that the rate of corrosion is increased with increasing the temperature at the same pH.

Downloads

Download data is not yet available.

References

[1] A. Pardo, M.C. Merino and E. Matykina: J.Corrosion ,50 , P.789-794, (2008).
[2] L.R. James and S.D. Philip :U.S. Patent , No.200401188274 , (2004).
[3] Y. Jinyee : M.Sc. Thesis, Umist, U.K , (2004) .
[4] T.Nagamine, A.Januszko and Y.Endo : Liquid Crystal , 32 , No.8 , P.985-993 , (2005).
[5] S. T. Arab and A. M. AI-Turkustani : Inte. J. Chem. , 12 , P.249-253 ,(2002).
[6] F. B. Ravari and A. Dadgarinezhad : Gazi Uni. J.of Sci. , 25, No.4 , P.835-842, (2012).
[7] E.C. Franch ,R.L. Mortin and J.A. Damgherty: Corrosion and Its Inhibition in Oil and Gas Wells , Nace Houston , P.1-25, (1993).
[8] A.M. Abdel - Gaber , B.A. Abd - Elnabey , I.M. Sidahmed , A.M. El-Zayady and M.Saadauy : J. Corro. Sci. ,62 , No.4 , P.293-297, (2006).
[9] M. A.Blankson and S.Erdem: Cons. and Building Materials , 77 , P. 59–65 , (2015).
[10] A.E. Pereira and M.F. Tavares : J. Chromatograohy, 105 , No.1 , P.303-308 , (2004).
[11] E.Bardal : Corrosion and Protection , 2nd Ed , Springer, N. Y. , USA , (2003) .
[12] N. A. Nagm and M. F. Zake : J. Corr. Sci. and Engineering ,10 , No. 32 , P.1-9 , (2007) .
[13] M. Bouklah and B. Hammouti : PortugaliaeElectrochimcaActa , 24 , P.457-468 , (2006) .

Downloads

Published

2018-04-02

How to Cite

kadhum, M. yousif, Bkhakh, C. K., & Albehadili, M. H. (2018). The Effect of Sodium Hydroxide Solutions with Different Ph on the Corrosion Of Iron Alloy (C1010) In Industrial Water. JOURNAL OF ADVANCES IN CHEMISTRY, 15(1), 6136–6141. https://doi.org/10.24297/jac.v15i1.7134

Issue

Section

Articles